Soft Magnetic Alloys Have High Adaptability And Precision Processing Capabilities In The (MIM) Process. With Excellent Magnetic Permeability And Low Loss Characteristics, The MIM Process Can Make Materials Into Complex Micro Parts (Such As Thin Walls And Special-Shaped Structures) Through Fine Powder Metallurgy Technology, Avoiding Material Waste Or Performance Damage Caused By Traditional Machining. It Not Only Retains The High Magnetic Properties Of The Material, But Also Achieves Cost Control For Mass Production Of Small And Medium-Sized Precision Parts.
The MIM Process Greatly Reduces The Internal Porosity Of The Material Through Uniform Mixing And High-Pressure Injection. After Sintering, It Can Form A Dense Organization With More Consistent Magnetic Domain Arrangement, Thereby Improving The Stability Of Magnetic Response. It Is Suitable For Manufacturing High-Frequency Electronic Devices, Micro Sensors And Other Industrial Fields That Have Strict Requirements On Dimensional Accuracy And Electromagnetic Efficiency.
Lead Time: < 15 Days
Tolerances: ±0.3% ~ ±0.5%
Max Part Size: Please Contact Us.
Available Soft Magnetic Alloys at Dazao: Fe-Ni50,Fe3Si,FeCo50,FeCoV etc .
Fe-Ni50
Small Parts With Complex Shapes And Precise Dimensions Can Be Manufactured Efficiently While Ensuring That The Material's High Magnetic Permeability And Low Loss Characteristics Are Stably Retained.
Soft Magnetic Alloys Fe-Ni50 Properties
|
Tensile Strength, Yield (MPa) |
Fatigue Strength (MPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
300-600 |
150-250 |
5-15 |
120-180 |
7.9-8.2 |
Fe3Si
It Can Efficiently Manufacture Complex Micro Parts, Has Strong Magnetism And Low Loss After Molding, And Is Suitable For The Production Of Precision Electronic Components.
Soft Magnetic Alloys Fe3Si Properties
|
Tensile Strength, Yield (MPa) |
Fatigue Strength (MPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
250-500 |
120-200 |
1-5 |
120-180 |
7-7.4 |
FeCo50
It Can Efficiently Mold Complex Precision Parts, Has High Magnetic Permeability And Low Loss, And Is Suitable For Mass Production Of Small High-Performance Magnetic Devices.
Soft Magnetic Alloys FeCo50 Properties
|
Tensile Strength, Yield (MPa) |
Fatigue Strength (MPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
450-800 |
250-350 |
2-5 |
180-250 |
7.9-8.3 |
FeCoV
It Can Quickly Manufacture Small Precision Parts With Complex Shapes, And Still Maintain Excellent High Magnetic Permeability And Low Magnetic Loss Characteristics After Sintering, Making It Suitable For Mass Production Of Micro Electromagnetic Components.
Soft Magnetic Alloys FeCoV Properties
|
Tensile Strength, Yield (MPa) |
Fatigue Strength (MPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
300-600 |
150-250 |
2-8 |
200-300 |
7.8-8.2 |