Aluminum Is The Most Common Nonferrous Metal On The Market And Is Highly Regarded For Its Low Density, High Strength-To-Weight Ratio, Durability, Natural Corrosion Resistance, Thermal Properties And Other Advantages. Dazao Provides High-Quality Aluminum Fabrication Services To A Wide Range Of Industries, Covering A Wide Range Of Fields Such As Automotive, Aerospace, Construction And Electronics. Our Aluminum Fabrication Services Include: Custom Aluminum Fabrication, CNC Machining, Sheet Metal Fabrication, Precision Laser Cutting, Welding, Finishing And More. Our Extensive Industry Experience And In-Depth Understanding Of Manufacturing Processes Ensure That We Can Manufacture Aluminum Parts According To Our Customers' Specific Needs. Coupled With Our Vast Manufacturing Network, You Can Rest Assured That Your Aluminum Parts Will Meet Your Schedule And Meet The Highest Quality Standards.
Lead Time: < 15 Days
Wall Thickness: Custom
Tolerances: ±0.1mm~ ±1.0mm
Max Part Size: Please Contact Us.
Available Aluminum at Dazao: Aluminum 2024, 5052, 6061, 6063, 6082, 7075 etc.
Aluminum
2024
It Has High Strength And Light Weight, But Is Prone To Cracking During Processing And Has Weak Corrosion Resistance, Requiring Surface Protection Treatment.
Aluminum 2024 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
325 |
140 |
20 |
120 |
2.78 |
Aluminum
5052
This Aluminum Alloy Has Magnesium As The Main Alloying Element. Since It Does Not Contain Copper In Its Composition, It Has Excellent Corrosion Resistance. Although 5052 Cannot Be Heat Treated, It Has The Highest Strength Among The Non-Heat Treatable Alloys. In Addition, The Alloy Also Has Better Formability Than The 3 Series Alloys. It Is Often Used To Make Fuel Tanks And Highway And Road Signs.
Aluminum 5052 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
193 |
117 |
18 |
60 |
2.68 |
Aluminum
6061
This Is One Of The Most "Versatile" Aluminum Alloys. The Main Alloying Elements Are Magnesium And Silicon, And It Can Be Heat Treated. Bending 6061 Aluminum Alloy After Reaching The High Tempering Temperature Is Not Recommended, As It Is Very Susceptible To Cracking. This Aluminum Alloy Can Be Used For Sheet Metal Parts, But It Requires Some Care And Preparation.
Aluminum 6061 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
276 |
96 |
17 |
95 |
2.7 |
Aluminum
6063
It Is Easy To Shape And Has A Smooth Appearance After Surface Treatment, But Has Medium Strength And Is Prone To Cracking When Bent. It Is Suitable For Parts That Have High Requirements On Appearance But Not Strict Requirements On Load-Bearing.
Aluminum 6063 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
214 |
68.9 |
12 |
73 |
2.7 |
Aluminum
6082
It Has Moderate Strength, Is Easy To Shape And Has Good Rust Resistance. It Is Not Easy To Warp After Processing, But Its Texture Is Hard And It Wears Cutting Tools Quickly.
Aluminum 6082 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
260 |
97 |
10-12 |
95 |
2.7 |
Aluminum
7075
The Material Is Light And Very Hard, Requires A Lot Of Force To Process And Is Prone To Cracking. It Is Suitable For Parts That Require High Strength But Has A High Production Cost.
Aluminum 7075 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
490 |
160 |
11 |
147 |
2.83 |