Stainless Steel Is Widely Used In Sheet Metal Fabrication And Is The Ideal Type Of Stainless Steel For Sheet Metal Fabrication Due To Its Excellent Formability, Ductility And Weldability. These Alloys Contain High Levels Of Chromium And Nickel, Making Them Far More Corrosion Resistant Than Standard Steels.
They Have Excellent Corrosion Resistance, Good Mechanical Properties And Superb Formability. These Properties Make Them Ideal For Sheet Metal Parts Exposed To Corrosive And Extreme Environments, Such As In The Marine, Aerospace And Chemical Processing Industries.
Lead Time: < 15 Days
Wall Thickness: Custom
Tolerances: ±0.1mm~ ±1.0mm
Max Part Size: Please Contact Us.
Available Stainless Steel at Dazao: Stainless Steel 303, 304, 316, 416, 17-4PH, 15-5 etc.
Stainless Steel
303
It Is Easy To Cut And Shape, Suitable For Making Complex Parts, But It Is Prone To Problems During Welding And Its Rust Resistance Is Not As Good As The Common 304 Stainless Steel.
Stainless Steel 303 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
240 |
77.2 |
50 |
160 |
8 |
Stainless Steel
304
Good Corrosion Resistance And Excellent Formability Make It Ideal For Manufacturing Sheet Metal Components. Applications Include Food Processing Equipment Such As Storage Tanks And Structural Supports.
Stainless Steel 304 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
215 |
77 |
70 |
123 |
8 |
Stainless Steel
316
Rust-Resistant And Durable, Its Common Applications Include Parts Exposed To Corrosive Environments, Such As Chemical Storage Tanks Or Marine Equipment.
Stainless Steel 316 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
205 |
74 |
40 |
187 |
8.03 |
Stainless Steel
416
It Has Excellent Cutting Performance And Low Cost, But It Is Easy To Produce Pores During Welding And Its Corrosion Resistance Is Weaker Than 304/316. It Is Suitable For Making Parts With High Precision Requirements But Low Environmental Corrosion.
Stainless Steel 416 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
275 |
83 |
30 |
156 |
7.8 |
Stainless Steel
17-4PH
High Strength, Good Corrosion Resistance, Easy To Form In Annealed State.
Stainless Steel 17-4PH Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
1379 |
77.4 |
7 |
419 |
7.8 |
Stainless Steel
15-5
High Strength, Corrosion Resistance, Easy To Weld And Form, And Attention Should Be Paid To Springback Control During Complex Bending.
Stainless Steel 15-5 Properties
|
Tensile Strength, Yield (MPa) |
Shear Modulus (GPa) |
Elongation at Break (%) |
Hardness (Brinell) |
Density (g/cm³) |
|
1280 |
77 |
10 |
388 |
7.8 |